COMPLEX MODIFICATION OF SECONDARY SILUMINS
DOI:
https://doi.org/10.15802/stp2014/33180Keywords:
silumins, intermetallic phases, structure, shape parameter, mechanical properties, refining and modifying treatmentAbstract
Purpose. Development of scientific and technological bases of formation of the specified secondary hypoeutectic (АK8M3) and eutectic (АК12М2MgН) silumins' structure; and increasing their mechanical and service properties' indices in the cast state and after heat treatment up to the level of primary alloys. Methodology. Determination of the chemical composition was conducted by spectral analysis on the spark spectrometer «SPECTROLAB» (Germany). Metallographic analysis was performed on the microscopes МIМ-7 and МIМ-8, and also by the high definition metallography method using the raster electronic microscope «JSMT-300» (Japan). Heat treatment of aluminum alloys was carried out applying T1 and T5 modes according to State Standard of Ukraine 2839-94 (GOST 1583-93). Standard techniques were used during the determination of mechanical properties. The temperature coefficient of linear expansion for the piston alloy АK12М2МgH (AL25) was determined using the specimens Ø with the diameter of 3.5 mm and length of 50 mm with the use of Shevenard optical quartz dilatometer. High temperature fracture resistance was determined according to State Standard 10145-81 as the time before fracture of the specimen at specified stress of 50 MPa and temperature of 300°С. Findings. The technology of obtaining alloys from charge, which consists of 100 % scrap and production wastes has been developed and implemented into production. This technology provides obtaining of metal of the guaranteed chemical composition and high quality with the reduction of energy costs for melting. Originality. The regularities of the formation of the structural and phase state and the level of physical and mechanical properties of eutectic and secondary hypoeutectic silumins depending on the refining and modifying processes have been established. The generalization of regularities of the secondary silumins' fracture has been carried out. Quantitative characteristics of the intermetallic phases' role in the fracture mechanisms and aluminum alloys' mechanical properties level formation have been obtained. Practical value. Structure formation processes of secondary aluminium alloys depending on their production technology have been studied. Highly efficient refining and modifying complexes for treatment of secondary hypoeutectic and eutectic aluminum alloys have been developed and the optimal quantity of modifiers depending on the charge quality has been determined.
References
Aleksakhin A.V., Khmelnitskaya N.V., Sivayeva Ye.K. Effektivnost ispolzovaniya vtorichnykh alyuminiyevykh splavov v liteynom proizvodstve [Efficiency of using the secondary aluminium alloys in foundry production]. Tezisy dokladov Vserossiyskoy konferentsii «Ekonomicheskiye problemy liteynogo proizvodstva Rossii» [Proc. of the All-Russian Conf. "Economic problems of foundry production in Russia"]. Penza, 1991, pp. 52-54.
Vozdvizhenskiy V.M., Grachev V.A., Spasskiy V.V. Liteynyye splavy i tekhnologiya ikh plavki v mashinostroyenii [Foundry alloys and technology of their melting in mechanical engineering].Moscow, Mashinostroyeniye Publ., 1984. 432 p.
Volchok I.P., Mityayev A.A. Povysheniye kachestva retsirkuliruyemykh alyuminiyevykh splavov [Increasing of the quality of the recycled aluminium alloys]. Visnyk dvyhunobuduvannia [Bulletin of aeroenginebuilding], 2004, issue 3, pp. 103-107.
Volchok I.P., Mitiaiev O.A., Riazanov S.H. Rafinuiuche-modyfikuiuchyi kompleks dlia obrobky aliuminiievykh splaviv [Refining and modifying complex for treatment of aluminium alloys]. Zbirnyk naukovykh prats X Mizhnarodnoi naukovo-tekhnichnoi konferentsii Zaporizhzhia «Nemetalevi vkraplennia i hazy u lyvarnykh splavakh» [Proc. of the 10th Int. Scientific and Technical Conf. of Zaporizhzhia «Non-metallic inclusions and gases in foundry alloys»]. Zaporizhzhia, 2003, p. 220.
Havrylenko B.B. Ekonomiko-pravovi vazheli ratsionalnoho pryrodokorystuvannia [Economical and law instruments of rational use of nature]. Zaporizhzhya, Polihraf Publ., 2004. 144 p.
GOST 10145-81. Metally. Metod ispytaniya na dlitelnuyu prochnost. [State Standard 10145-81. Metals. The method of testing of long-term strength].Moscow, Izd-vo standartov Publ., 1981. 12 p.
Zilberg Yu.Ya., Khrushchova K.M, Gershman G.B. Alyuminiyevyye splavy v traktorostroyenii [Aluminium alloys in tractor building].Moscow, Mashinostroyeniye Publ., 1971. 151 p.
Loza K.N. Vliyaniye modifitsirovaniya i termicheskoy obrabotki na formirovaniye struktury i svoystv vtorichnogo porshnevogo splava AL25. Kand, Diss. [Influence of modification and heat treatment on the formation of structure and properties of the secondary piston alloy AL25. Cand. Diss.]. Zaporozhye, 2012.
Lyutova O.V. Povysheniye liteynykh svoystv vtorichnykh alyuminiyevykh splavov [Increasing of foundry properties of secondary aluminium alloys]. Nauka ta prohres transportu. Visnyk Dnipropetrovskoho natsionalnoho universytetu zaliznychnoho transportu − Science and Transport Progress. Bulletin of Dnipropetrovsk National University of Railway Transport, 2013, no. 3 (45), pp. 53-59.
Mityayev A.A. Kompleksnaya rafiniruyushche-modifitsiruyushchaya obrabotka alyuminiyevykh splavov [Complex refining and modifying treatment of aluminium alloys]. Stroitelstvo, materialovedeniye, mashinostroyeniye [Consruction, material science, machine building], issue 45, part 2, pp. 138-142.
Mityayev A.A. Povysheniye kachestva pereplava zagryaznennoy alyuminiyevoy struzhki [Increasing of the remelting quality of the contaminated aluminium chip]. Vіsnyk Dnіpropetrovskoho natsіonalnoho unіversytetu zalіznichnoho transportu іmenі akademіka V. Lazariana [Bulletin of Dnipropetrovsk National University of Railway Transport named after Academician V. Lazaryan], 2008, issue 22, pp. 175-180.
Volchok I.P., Mitiaiev O.A. Modyfikator dlia aliuminiievykh splaviv [Modifier for aluminium alloys]. Patent UA, no. 2002108343, 2003.
Volchok I.P. Mitiaiev O.A., Ostrovska A.Ye., Skuibida O.L. Modyfikator aliuminiievykh splaviv [Modifier of aluminium alloys]. Patent UA, no. u200902454, 2009.
Loza K.M., Mitiaiev O.A., Volchok I.P. Modyfikuvalnyi kompleks dlia aliuminiievykh splaviv [Modifying complex for aluminium alloys]. Patent UA, no. u200905914, 2009.
Shyrokobokova N.V., Mitiaiev O.A., Volchok I.P., Kiurchev S.V., Kolodii O.S. Rafinuvalno-modyfikuvalnyi kompleks dlia aliuminiievykh splaviv [Refining and modifying complex for aluminium alloys]. Patent UA, no. u201112705, 2012.
Belikov S., VolchokI., Mityayev O. The nanomodifier of aluminium alloys. Aims for future of engineering science. AFES 2006. Switzerland, 2006, pp. 191-193.
Vakulenko I.A, Nadezhdin Yu.L., Sokirko V.A, Volchok I.P., Mityayev A.A. Electric pulse treatment of welded joint of aluminum alloy. Nauka ta prohres transportu. Visnyk Dnipropetrovskoho natsionalnoho universytetu zaliznychnoho transportu − Science and Transport Progress. Bulletin of Dnipropetrovsk National University of Railway Transport, 2013, no. 4 (46), pp. 73-82.
Pietrowski S., Gumienny G., Pisarek B., Wladysiak R. Kontrola produkcji wysokojakosciowych stopow odlewniczych metoda ATD [Production control of advanced casting alloys with TDA method]. Archiwum technologii maszyn i automatyzacji, 2004, vol. 24, issue 3, pp. 131-144.
Lipinski T. Improvement of mechanical properties of AlSi7Mg alloy with fast cooling homogeneous modifier. Archives of foundry engineering. Katowice-Gliwice, 2008, vol. 8, issue 1/2008, pp. 85-88.
Mityayev A., Belikov S. Improvement of quality of secondary aluminium alloys in conditions of mass production. Archives of metallurgy and materials. Warszawa-Krakow, 2007, vol. 52, no. 3, pp. 521-524.
Klyszewski A., Lech-Grega M., Szymanski W., Zelechowski J. The structure and properties of sheets made from aluminium and aluminium alloys for use in transport industry. Proc. of 9th Int. Conf. «Aluminium in transport 2003». Cracow-Tomaszowice, 2003, pp. 203-217.
Downloads
Published
How to Cite
Issue
Section
License
Copyright and Licensing
This journal provides open access to all of its content.
As such, copyright for articles published in this journal is retained by the authors, under the terms of the Creative Commons Attribution 4.0 International License (CC BY 4.0). The CC BY license permits commercial and non-commercial reuse. Such access is associated with increased readership and increased citation of an author's work. For more information on this approach, see the Public Knowledge Project, the Directory of Open Access Journals, or the Budapest Open Access Initiative.
The CC BY 4.0 license allows users to copy, distribute and adapt the work in any way, provided that they properly point to the author. Therefore, the editorial board of the journal does not prevent from placing published materials in third-party repositories. In order to protect manuscripts from misappropriation by unscrupulous authors, reference should be made to the original version of the work.