INFLUENCE OF THE CAST IRON’S CHEMICAL COMPOSITION ON THE INTERPHASE DISTRIBUTION OF CR AFTER ANNEALING AT 690 °C

Authors

DOI:

https://doi.org/10.15802/stp2017/109583

Keywords:

cast iron, chromium, distribution, carbide, metallic base

Abstract

Purpose. The article is aimed to determine effect of the chemical composition of Fe-C-Cr-Mn-Ni cast iron on the chromium content in the metallic base, carbides and the coefficient of interphase distribution of chromium after annealing at 690 ° С (КРСr690). Methodology. Cast irons containing 1.09–3.91% C; 11.43–25.57% Cr; 0.6–5.4% Mn; 0.19–3.01% Ni and 0.8–1.2% Si were investigated. The analysis of chromium distribution was carried out using mathematical statistics methods. Cast iron was melted in induction furnace with a capacity of 60 kg. Findings. The use of methods of active planning of the experiment 24-1 allowed us to establish regression dependencies of the chromium concentration in the base and carbides, as well as its interphase distribution coefficient on the С, Mn, Cr and Ni content in the cast iron. Chromium, after annealing, was mainly concentrated in carbides. The chromium content of the base varies from 3.94% at 3.23% C, 5.4% Mn, 11.43% Cr and 3.01% Ni to 17.43% at 1.09% C, 0.60% Mn, 25.57% Cr and 1.32% Ni. The minimum value of the distribution coefficient of CRC690 was 2.1 in cast iron, of composition 1.09% C, 0.6% Mn, 11.43% Cr and 0.19% Ni, maximum 9.4 at 3.91% C, 0, 6% Mn, 11.43% Cr and 3.01% Ni. The distribution of chromium was determined by the amount and type of carbides formed. During annealing, the carbides’ composition was formed as a result of carbide-forming elements contention and replacement of iron and manganese atoms by chromium atoms. Originality. Authors obtained regression dependences of the chromium content in the base, carbides and its interfacial distribution coefficient on the chemical composition of Fe-C-Cr-Mn-Ni cast iron after annealing at 690 ° C. Practical value. The obtained dependencies allow predicting the chromium content in the metallic base and may be used during the elaboration of the new wear resistant cast irons compositions, as well as in the choice of heat treatment regimes.

Author Biographies

V. V. Netrebko, Zaporizhzhia National Technical University

Dep. «Equipment and Technology of Welding Production», Zhukovskyi St., 64, Zaporizhzhia, Ukraine, 69063,
tel. +38 (050) 486 27 40

I. P. Volchok, Zaporizhzhia National Technical University

Dep. «Composite and Powder Materials and Technologies», Zhukovskyi St., 64, Zaporizhzhia, Ukraine, 69063,
tel. +38 (061) 769 83 51

References

Vakulenko, I.O. (2010). Strukturnyi analiz v materialoznavstvi. Dnipropetrovsk: Makovetskyi.

Kutsova, V. Z., Kovzel, M. A., Kravchenko, A. V., & Zhivotovich, A. V. (2007). Vliyaniye rezhemov termicheskoy obrabotki na raspredeleniye legiryshchekh elementov v vysokokhromistom chugune. Metal Science and Heat Treatment, 3 (2), 33-51.

Volchok, I.P., Netrebko, V. V. (2015). Effect of alloying and heat treatment on the distribution of the elements and properties of high chrome cast iron. Scientific bulletin of DSEA, 3 (18Е), 52-59.

Alloy cast iron for castings of special properties. Grades, State Standard 7769-82 (1982).

Gudremon, E. (1966). Spetsialnyye stali (Vol. 1).Moscow: Metallurgiya.

Gulyaev, A. P. (1978). Metallovedeniye.Moscow: Metallurgiya.

Kutsova, V. Z., Kovzel, M. A., & Kravchenko, A. V. (2008). Vliyaniye temperatury nagreva na formirovaniye struktury, fazovyy sostav i svoystva vysokokhromistykh chugunov v iskhodnom i termoobrabotannom sostoyanii. Physical Metallurgy and Heat Treatment of Metals, 1, 35-50.

Malakhov, A. I., & Zhukov, A. P. (1978). Osnovy metallovedeniya i teorii korrozii.Moscow: Vysshaya shkola.

Еfremenko, V. G., Cheiliakh, О. P., Kozarevska, T. V., Shimizu, K., Chabak, Y. G., & Efremenko, О. V. (2014). Phase chemical elements distribution in complex-alloyed white cast iron. Reporter of the Priazovskyi state technical university. Section: Technical sciences, 28, 89-99.

Netrebko, V. V. (2016). About the issue of carbides Fe3C and Fe7C3 formation in high-chromium cast irons. Science and Transport Progress, 3 (63), 138-147. doi: 10.15802/stp2016/74736

Netrebko, V. V., Volchok, I. P. (2016). Peculiarities of heat treatment of high-chromium cast irons alloyed by Mn and Ni. Innovative materials and technologies in metallurgy and mechanical engineering, 1, 53-57.

Silman, G. I. (2005). Diagramma sostoyaniya splavov sistemy Fe-C-Mn i nekotoryye strukturnyye effekty v etoy sisteme. Mezhfaznoye raspredeleniye margantsa. Metal Science and Heat Treatment, 2, 11-15.

Kirillov, A. A., Belov, V. D., Rozhko, Y. V., Diadkova, A. Y., & Zueva, I. E. (2007). Strukturno i nestrukturno chuvstvitelnyye svoystva khromistykh chugunov. Stahl und Eisen, 9, 7-13.

Chabak, Y. G., Еfremenko, V. G., & Stanishevskiy, R. R. (2011). Structure changes in the complex-alloyed white cast iron during destabilizing heating. Bulletin of Dniproperovsk National University of Railway Transport named after Academician V. Lazaryan, 38, 229-232.

Cheylyakh, A. P. (2003). Ekonomnolegirovannye metastabilnyye splavy i uprochnyayushchiye tekhnologii. Kharkov: National Science Center Kharkov Institute of Physics and Technology.

Tsypin, I. I. (1983). Belyye iznosostoykiye chuguny. Struktura i svoystva. Moscow: Metallurgiya.

Tsypin, I. I. (2000). Belyye iznosostoykiye chuguny – evolyutsiya i perspektivy. Foundry, 9, 15-16.

Kopyciński, D., Kawalec, M., Szczęsny, A., Gilewski, R., & Piasny, S. (2013). Analysis of the Structure and Abrasive Wear Resistance of White Cast Iron with Precipitates of Carbides. Archives of Metallurgy and Materials, 58 (3), 973-976. doi: 10.2478/amm-2013-0113

Belikov, S., Volchok, I., & Netrebko, V. (2013). Manganese influence on chromium distribution in high-chromium cast iron. Archives of Metallurgy and Materials, 58 (3), 895-897. doi: 10.2478/amm-2013-0095

Gierek, A., & Bajka, L. (1976). Zeliwo stopowe jako tworzywo konstrukcyjne.Katowice: Slask Publ.

Downloads

Published

2017-09-06

How to Cite

Netrebko, V. V., & Volchok, I. P. (2017). INFLUENCE OF THE CAST IRON’S CHEMICAL COMPOSITION ON THE INTERPHASE DISTRIBUTION OF CR AFTER ANNEALING AT 690 °C. Science and Transport Progress, (4(70), 60–70. https://doi.org/10.15802/stp2017/109583

Issue

No. 4(70) (2017)

Section

MATERIAL SCIENCE

License

Copyright and Licensing

This journal provides open access to all of its content.
As such, copyright for articles published in this journal is retained by the authors, under the terms of the Creative Commons Attribution 4.0 International License (CC BY 4.0). The CC BY license permits commercial and non-commercial reuse. Such access is associated with increased readership and increased citation of an author's work. For more information on this approach, see the Public Knowledge Project, the Directory of Open Access Journals, or the Budapest Open Access Initiative.

The CC BY 4.0 license allows users to copy, distribute and adapt the work in any way, provided that they properly point to the author. Therefore, the editorial board of the journal does not prevent from placing published materials in third-party repositories. In order to protect manuscripts from misappropriation by unscrupulous authors, reference should be made to the original version of the work.